Analysis of Operational Degradation of Railway Wheel Treads

Autoři: Švanda Pavel | Schmidová Eva | Beneš Libor

Rok: 2006

Druh publikace: ostatní - přednáška nebo poster

Název zdroje:

Název nakladatele:

Místo vydání:

Strana od-do:

Tituly:

Jazyk	Název	Abstrakt	Klíčová slova
cze	Anlýza provozního opotřebení jízdní plochy železničního kola	Description of structural changes in railway wheels during operational period. The nature of structure was investigated using light microscopy and microhardness. Our study characterized two basic mechanisms of cracking formation - thermal initialization and contact-fatigue damage. These two mechanisms can generate different structures, but both contribute to irreversible degradation on the surface of railways wheels.	wheel treads, structure analysis
eng	Analysis of Operational Degradation of Railway Wheel Treads	Description of structural changes in railway wheels during operational period. The nature of structure was investigated using light microscopy and microhardness. Our study characterized two basic mechanisms of cracking formation - thermal initialization and contact-fatigue damage. These two mechanisms can generate different structures, but both contribute to irreversible degradation on the surface of railways wheels.	wheel treads, structure analysis

Vyhledávání