Corrosion Process in Area of Elastomer - Steel Cord in the Tires

Autoři: Drdáková Jozefína | Krmela Jan | Krmelová Vladimíra

Rok: 2013

Druh publikace: kapitola v odborné knize

Název zdroje: New trends in the field of materials and technologies engineering

Název nakladatele: Association of Quality and Production Managers - Publishing House

Místo vydání: Częstochowa

Strana od-do: 51-58

Tituly:

Jazyk	Název	Abstrakt	Klíčová slova
cze	Korozní procesy v oblasti elastomer - ocelový kord v pneumatikách	Článok sa zaoberá mikrolokalitou systému elastomér - oceľový kord v plášťoch pneumatík po degradačnom procese s využitím mikroskopického pozorovania na elektrónovom rastrovacom mikroskope. V prípade degradačného procesu plášťov pneumatík môže na rozhraní medzi elastomérnou matricou a oceľokordom dochádzať k porušovaniu. U takto znehodnoteného rozhrania, povrchová úprava oceľokordov stráca svoju funkciu kompaktnosti systému elastomér- oceľový kord a tým je ovplyvnená kompaktnosť štruktúry celého plášťa. Pre metalografické vzorky boli vybrané skúšobné vzorky z plášťa pneumatiky, ktoré boli exponované v koróznej komore soľnou hmlou 256 hodín. V článku sú uvedené vybrané výsledky z rastrovaciej elektrónovej mikroskopie. Pre hodnotenie degradačného procesu, v tomto prípade vplyvu korózneho pôsobenia, boli použite tieto analýzy: plošná, bodová, líniová.	Pneumatika; plášť pneumatiky; degradace; ocelový kord; elastomer; mikrostruktura; elektronový mikroskop
eng	Corrosion Process in Area of Elastomer - Steel Cord in the Tires	The given paper deals with microlocation area of the system where there is the connection area between the elastomer and steel cord in relation to tire-casing after degradation corrosion process. The electron scanning microscope has been used during the microscopic observation of this mentioned area. In the case of the degradation process of tire-casings, the rupture can be observed at the interface between the elastomeric matrix and steel cord. If the interface is ruptured in such a way, the surface design loses its primary or given function relating to compactness of the system: elastomer - steel cord. The tested metallographic samples were obtained from one tire-casing and they were exposed to the corrosive salt environment for 256 hours. Some chosen results of scanning electron microscopy are presented in the paper. In the relation to the corrosion effect, the following analyses were used for evaluation of the degradation process: surface, point, line.	Tire; tire-casing; corrosion process; degradation; steel cord; elastomer; microstructure; electron microscope